CP Cellulose Acetate Propionate

STRUCTURE:

SPECIFIC DENSITY:

WATER ABSORPTION RATE (%):

ELONGATION (%):

TENSILE STRENGTH (psi):

COMPRESSION STRENGTH (psi):

FLEXURAL STRENGTH (psi):

FLEXURAL MODULUS (psi):

IMPACT (IZOD ft. lbs/in):

HARDNESS:

FABRICATION
- BONDING:
- ULTRASONIC WELDING:
- MACHINING:

DEFLECTION TEMPERATURE (deg. F)
- @ 66 psi:
- @ 264 psi:

UTILIZATION TEMPERATURE (deg. F)
- min:
- max:

MELTING POINT (deg. F):

COEFFICIENT OF EXPANSION:

ARC RESISTANCE:

DIELECTRIC STRENGTH (kV/mm):

TRANSPARENCY:

UV RESISTANCE:

CHEMICAL RESISTANCE
- ACIDS:
- ALKALIS:
- SOLVENTS:

A

1.22

2

50

6000

8500

8500

180000

1.5

R80


- P
- P
- P


- 194
- 167


-40
212

248

0.00007

180

13

C

G


P
P
P