PA12G - Polyamide 12, 30% Glass Filled

STRUCTURE:

SPECIFIC DENSITY:

WATER ABSORPTION RATE (%):

ELONGATION (%):

TENSILE STRENGTH (psi):

COMPRESSION STRENGTH (psi):

FLEXURAL STRENGTH (psi):

FLEXURAL MODULUS (psi):

IMPACT (IZOD ft. lbs/in):

HARDNESS:

FABRICATION
- BONDING:
- ULTRASONIC WELDING:
- MACHINING:

DEFLECTION TEMPERATURE (deg. F)
- @ 66 psi:
- @ 264 psi:

UTILIZATION TEMPERATURE (deg. F)
- min:
- max:

MELTING POINT (deg. F):

COEFFICIENT OF EXPANSION:

ARC RESISTANCE:

DIELECTRIC STRENGTH (kV/mm):

TRANSPARENCY:

UV RESISTANCE:

CHEMICAL RESISTANCE
- ACIDS:
- ALKALIS:
- SOLVENTS:

Cr

1.23

0.3

5

13500

16000

4400

360000

4.4

R110


G
G
P


230
300


-110
230

350

0.000016

120

17

0

G


P
P
G